الملخصThe current article deals with the development of different novel, tailor-made polyolefin formulations exhibiting both low flammability and high weathering resistance, so as to provide value-added polyethylene grades with extended service lifetime. Two low-density (LDPE) and one linear low-density (LLDPE) polyethylene grades were modified via melt compounding with an additive system comprising: (a) a nitrogen-phosphorous intumescent system for flame retardance and (b) a hindered amine light stabilizer and a benzophenone-type UV absorber for UV/heat stabilization, at a total loading of 30-35 wt%. The target was to reach V0 classification in UL94V flammability tests, while to a large extent maintaining the mechanical properties, such as, tensile and impact strength of the investigated polymers, thus ensuring that the additives do not interfere significantly with the material quality. Subsequently, the compounds were subjected to separate artificial UV and heat aging at 100 C for 1500 h; the formulations showed good flame retardance, even after prolonged artificial weathering, but there was an observable, although acceptable, decrease in the mechanical properties. Nevertheless, all the results show that the developed polyethylene compounds are very promising for outdoor applications, such as, irrigation piping and profiles, where long-term weathering stability is important, and where flame retardance is important for safety during storage.
راعي المشروعThis publication was made possible by the NPRP award (NPRP 9-161-1-030) from the Qatar National Research Fund (a member of The Qatar Foundation). We are also grateful to BASF and Sabo for supplying the additives at no cost. We further express our gratitude to Dr. Mabrouk Ouederni from QAPCO for providing us with the three polyethylene grades. The statements made herein are solely the responsibility of the author(s).
اللغةen
الناشرJohn Wiley and Sons Inc
الموضوعaging
flame retardance
mechanical properties
polyolefins
العنوانDevelopment of value-added polyethylene grades with extended service lifetime: Weathering resistant flame retarded materials for outdoor applications