تاريخ النشر2019
اسم المنشورTribology Transactions
المصدرScopus
معرّف المصادر الموحدhttp://dx.doi.org/10.1080/10402004.2019.1634227
معرّف المصادر الموحدhttp://hdl.handle.net/10576/39403
الملخصIn order to improve the toughness of Ni-P coatings, Ti particles were introduced into the plating solution to produce a Ni-P-Ti composite coating (on API-X100 steel), which was subsequently annealed to form superelastic NiTi precipitates within the coating. The effect of Ti content on deposition rate and surface morphology of Ni-P-Ti coatings was studied. A detailed investigation of the influence of Ti content and annealing on the microstructure, microhardness, and scratch behavior of Ni-P-Ti composite coatings was carried out. Further, scratch resistance and toughening mechanisms, namely, crack deflection, crack bridging, and crack shielding, are discussed. The NiTi precipitates greatly improved the cracking and scratch resistance as a result of the superelastic NiTi toughening effect.
راعي المشروعThis publication was made possible by NPRP Grant #NPRP8-1212-2-499 from the Qatar National Research Fund (a member of Qatar Foundation). The findings herein are solely the responsibility of the authors.
اللغةen
الناشرTaylor and Francis Inc.
الموضوعNi-P-Ti-based coatings
scratch resistance
toughening mechanisms
toughness
العنوانSynthesis and Characterization of Scratch-Resistant Ni-P-Ti-Based Composite Coating
النوعArticle
الصفحات880-896
رقم العدد5
رقم المجلد62