Microstructure evolution and mechanical properties of twinned AZ31 alloy plates at lower elevated temperature
المؤلف | Zhang, Hua |
المؤلف | Liu, Yang |
المؤلف | Fan, Jianfeng |
المؤلف | Roven, Hans Jørgen |
المؤلف | Cheng, Weili |
المؤلف | Xu, Bingshe |
المؤلف | Dong, Hongbiao |
تاريخ الإتاحة | 2016-01-14T13:24:27Z |
تاريخ النشر | 2014-12 |
اسم المنشور | Journal of Alloys and Compounds |
المصدر | Scopus |
المعرّف | http://dx.doi.org/10.1016/j.jallcom.2014.07.045 |
الاقتباس | Zhang, H., Liu, Y., Fan, J., Roven, H.Jo., Cheng, W., Xu, B., Dong, H., "Microstructure evolution and mechanical properties of twinned AZ31 alloy plates at lower elevated temperature", (2014) Journal of Alloys and Compounds, 615, pp. 687-692 |
الرقم المعياري الدولي للكتاب | 0925-8388 |
الملخص | The AZ31 alloy plates were pre-rolled at room temperature along the transverse direction to introduce extension twinning. The effect of pre-existing twins on the mechanical properties of AZ31 alloy plates at lower elevated temperature was investigated in the current paper. The results revealed that the twinned AZ31 alloy plates exhibited higher strength at lower elevated temperature than the as-received plates without a large reduction in elongation, especially the yield strength increased by 36, 30 and 21 MPa at room temperature, 100 °C and 200 °C, respectively. The improved strength is attributed to the grain refinement by pre-existing {10–12} twin boundaries. Compared with the as-received AZ31 alloy plates, the twinned plates exhibited more pronounced flow softening at 200 °C, which can be interpreted by the dynamic recrystallization softening effect induced by pre-existing twins. |
راعي المشروع | This work is supported by the Program for New Century Excellent Talents in University (NCET-12-1040), National Natural Science Foundation of China (50901048 and 51174143), Shanxi Province Science Foundation for Youths (2013021013-4) and Advanced Programs of Department of Human Resources and Social Security of Shanxi Province for Returned Scholars (2012L003). |
اللغة | en |
الناشر | Elsevier Ltd |
الموضوع | Dynamic recrystallization Mechanical properties Metals and alloys Twinning |
النوع | Article |
الصفحات | 687-692 |
رقم المجلد | 615 |
تحقق من خيارات الوصول
الملفات في هذه التسجيلة
الملفات | الحجم | الصيغة | العرض |
---|---|---|---|
لا توجد ملفات لها صلة بهذه التسجيلة. |
هذه التسجيلة تظهر في المجموعات التالية
-
الأبحاث [1356 items ]