Show simple item record

AuthorSk, Mobbassar hassan
AuthorAbdullah, Aboubakr Moustafa
AuthorAl-Qahtani, Noora Hamad S
AuthorLaycock, Nick
AuthorRyan, Mary P
AuthorWilliams, David E
Available date2023-11-06T07:23:12Z
Publication Date2018
Publication NameQatar Foundation Annual Research Conference Proceedings
Identifierhttp://dx.doi.org/10.5339/qfarc.2018.EEPP605
CitationSk M et al. (2018). Effect of Trace 100 vppm H2S on the Corrosion Behaviour of Plain Carbon and Microalloyed Steels in a Predominant Sweet Environment in High Flow Regime. Qatar Foundation Annual Research Conference Proceedings 2018: EEPP605 http://doi.org/10.5339/qfarc.2018.EEPP605.
ISSN2226-9649
URIhttp://hdl.handle.net/10576/49046
AbstractWe investigate the effects of the presence of trace (100 vppm) H2S on the corrosion behaviour of plain carbon steel and its various micro-alloyed counterparts in a CO2 saturated (sweet) brine (0.5 M NaCl) environment, in a high flow regime (1000 RPM), at 80oC in a slightly acidic environment (pH 6.6). Potentiostatic current transients indicate that the presence of trace amount of trace H2S in a predominantly sweet regime, where the partial pressure ratio of CO2 and H2S (pCO2:pH2S) is ∼10000:1, shows a very different corrosion behaviour for both plain carbon steels and as well as micro-alloyed steels. In presence of trace H2S, current density starts dropping much earlier compared to H2S free standalone CO2 environment. Trace amount of H2S also induces faster passivation of the corrosion scale, especially for alloys with relatively high Mo (0.7 wt.%) and Ni (1.4 wt.%) content, suggesting that Mo and Ni have a strong effect in presence of trace H2S. On the basis of available literature, we speculate that the effects observed in presence of trace H2S is due to the formation of Mackinawite which forms on the steel surface immediately via solid state reaction and micro-alloying with some specific elements catalyzes the formation of mackinawite and/or assists formation of more stable sulfide phase(s), causing a faster current drop and passivation. Modeling of the hypothesis is currently in progress. Keywords: Micro-alloying, CO2 corrosion, Flow effect, RDE, Plain carbon steel, Cr-Mo-Ni steel. Figure: Potentiostatic current transient for various plain carbon and micro-alloyed steels. Condition - pH: 6.6, Temp: 80oC, Flow: 1000 RPM, @ anodic over potential: Open Circuit Potentials (OCP) +150 mV
Languageen
PublisherHamad bin Khalifa University Press (HBKU Press)
SubjectMicro-alloying
CO2 corrosion
Flow effect
RDE
Plain carbon steel
Cr-Mo-Ni steel
TitleEffect of Trace 100 vppm H2S on the Corrosion Behaviour of Plain Carbon and Microalloyed Steels in a Predominant Sweet Environment in High Flow Regime
TypeConference Paper
Issue Number1
Volume Number2018
dc.accessType Open Access