Morphology and magnetic properties of the ethylene-co-vinyl acetate/iron nanocomposite films prepared by implantation with Fe6+ ions
المؤلف | Božanić, Dušan K. |
المؤلف | Draganić, Ilija |
المؤلف | Bibić, Nataša |
المؤلف | Luyt, Adriaan S. |
المؤلف | Konstantinović, Zorica |
المؤلف | Djoković, Vladimir |
تاريخ الإتاحة | 2017-03-02T05:35:09Z |
تاريخ النشر | 2016-08 |
اسم المنشور | Applied Surface Science |
المعرّف | http://dx.doi.org/10.1016/j.apsusc.2016.04.020 |
الاقتباس | Dušan K. Božanić, Ilija Draganić, Nataša Bibić, Adriaan S. Luyt, Zorica Konstantinović, Vladimir Djoković, Morphology and magnetic properties of the ethylene-co-vinyl acetate/iron nanocomposite films prepared by implantation with Fe6+ ions, Applied Surface Science, Volume 378, 15 August 2016, Pages 362-367 |
الرقم المعياري الدولي للكتاب | 0169-4332 |
الملخص | Ethylene-co-vinyl acetate/iron nanocomposite films were fabricated by implantation with multiplecharged ions at different fluencies. The films obtained with ion fluency of 1 × 1017cm−2were used forspecific studies. It was found that spherical ∼1.5 nm diameter nanoparticles were formed upon implan-tation. They were clustered into a single 80 nm wide strip about 40 nm beneath the film surface. Themagnetic measurements of the film showed that the particles exhibit superparamagnetic behavior witha blocking temperature below 5 K. A second type of the samples was also prepared with ion fluencyof 1 × 1017cm−2, but prior to implantation, the iron was evaporated onto the co-polymer surface. Ananocomposite film of different morphology was obtained upon the implantation and the particles weremuch smaller (∼0.8 nm). The magnetic behavior of both the films was that of isolated nanoparticles,despite the high ion fluency of 1 × 1017cm−2. |
راعي المشروع | Ministry of Education, Science and Technological Development, Republic of Serbia (Project Nos. 172056, III45020 and III45018). |
اللغة | en |
الناشر | Elsevier |
الموضوع | Ion beam mixing Magnetic properties Multiple charged ions Nanocomposite Iron Ion implantation |
النوع | Article |
الصفحات | 362-367 |
رقم المجلد | 378 |