CoNi Nanoparticles/CNT Composite as Effective Anode for Direct Urea Fuel Cells
المؤلف | Barakat, Nasser |
المؤلف | Alajami1, Mohannad |
المؤلف | Ghouri, Zafar Khan |
المؤلف | Al-Meer, Saeed |
تاريخ الإتاحة | 2018-04-09T11:12:31Z |
تاريخ النشر | 2018-02-28 |
اسم المنشور | international journal of electrochemical science |
المعرّف | http://dx.doi.org/10.20964/2018.05.10 |
الاقتباس | Int. J. Electrochem. Sci., 13 (2018) 4693 – 4699, doi: 10.20964/2018.05.10 |
الملخص | CoNi nanoparticles/CNTs composite is introduced as workable anode in the direct urea fuel cells. The proposed anode was prepared by calcination under argon atmosphere of a dried cobalt acetate/nickel acetate/CNTs/ethanol slurry at 850 oC. The composition of the metal nanoparticles was optimized by synthesizing composites having different cobalt contents compared to nickel. The results indicated that the best performance is attributed to the anode containing nanoparticles having 10 wt% Co as the corresponding generated power was 3.95 mW/m2 which is 40 folds compared to that obtained from pristine nickel nanoparticles-containing anode (0.09 mW/m2). |
راعي المشروع | This Publication was made possible by NPRP grant # [8-1344-1-246] from the Qatar National Research Fund (a member of Qatar Foundation). The findings achieved herein are solely the responsibility of authors. |
اللغة | en |
الناشر | ESG. |
الموضوع | Direct urea fuel cells CoNi/CNTs composites Urea oxidation. |
النوع | Article |
الصفحات | 4693 – 4699 |
رقم المجلد | 13 |