الملخصFrom acidic NiP electroless bath, the co-deposition of TiNi nanoparticles in the NiP matrix to form novel NiP-TiNi nanocomposite coatings (NCCs) on top of API X100 carbon steel using several concentrations of TiNi nanoparticles (0.2, 0.4 and 0.8 g L−1 in the bath) is successfully achieved. The influence of the TiNi nanoparticles on the composition, deposition rate, thickness, and morphology of the NiP coating are investigated before and after annealing at 400 °C. The addition of TiNi nanoparticles into the NiP matrix leads to the transformation of the amorphous structure of the as-plated NiP into a semi-crystalline one. The microhardness of the composite coating significantly enhances with increasing the TiNi concentration up to 0.4 g L−1 and further improvement takes place after the heat treatment. The electrochemical impedance spectroscopy (EIS) and the colony counting method are carried out to assess the corrosion protection and antibacterial properties, respectively, of the as-deposited and the annealed coatings. The results demonstrate that there is an optimum concentration for the addition of TiNi (0.4 g L−1), which offers the composite coating with the highest corrosion protection (reaches to about 98%). Below and above this concentration as well as after the heat treatment, the improvement in the corrosion protection of the composite coatings slightly decreases. Besides, the NiP–TiNi NCCs have effective antibacterial properties as the cell viability of Escherichia coli decreases from 100 to 19%.
راعي المشروعThis work was supported by the NPRP grant # NPRP8-1212-2-499 from the Qatar National Research Fund (a member of Qatar Foundation). The statements made herein are solely the responsibility of the authors. Appendix A
اللغةen
الناشرElsevier B.V.
الموضوعAntibacterial
Composite coating
Corrosion resistant
Electroless NiP
Heat-treatment
TiNi
العنوانNovel electroless deposited corrosion — resistant and anti-bacterial NiP–TiNi nanocomposite coatings